This book presents the relationships between tensile damage and fracture, fatigue hysteresis loops, stress-rupture, fatigue life and fatigue limit stress, and stochastic loading stress. Ceramic-matrix composites (CMCs) possess low material density (i.e., only 1/4 - 1/3 of high-temperature alloy) and high-temperature resistance, which can reduce cooling air and improve structure efficiency. Understanding the failure mechanisms and internal damage evolution represents an important step to ensure reliability and safety of CMCs. This book investigates damage and fracture of fiber-reinforced ceramic-matrix composites (CMCs) subjected to stochastic loading, including: (1) tensile damage and fracture of fiber-reinforced CMCs subjected to stochastic loading; (2) fatigue hysteresis loops of fiber-reinforced CMCs subjected to stochastic loading; (3) stress rupture of fiber-reinforced CMCs with stochastic loading at intermediate temperature; (4) fatigue life prediction of fiber-reinforced CMCs subjected to stochastic overloading stress at elevated temperature; and (5) fatigue limit stress prediction of fiber-reinforced CMCs with stochastic loading. This book helps the material scientists and engineering designers to understand and master the damage and fracture of ceramic-matrix composites under stochastic loading.

This book presents the relationships between tensile damage and fracture, fatigue hysteresis loops, stress-rupture, fatigue life and fatigue limit stress, and stochastic loading stress. Ceramic-matrix composites (CMCs) possess low material density (i.e., only 1/4 - 1/3 of high-temperature alloy) and high-temperature resistance, which can reduce cooling air and improve structure efficiency. Understanding the failure mechanisms and internal damage evolution represents an important step to ensure reliability and safety of CMCs. This book investigates damage and fracture of fiber-reinforced ceramic-matrix composites (CMCs) subjected to stochastic loading, including: (1) tensile damage and fracture of fiber-reinforced CMCs subjected to stochastic loading; (2) fatigue hysteresis loops of fiber-reinforced CMCs subjected to stochastic loading; (3) stress rupture of fiber-reinforced CMCs with stochastic loading at intermediate temperature; (4) fatigue life prediction of fiber-reinforced CMCs subjected to stochastic overloading stress at elevated temperature; and (5) fatigue limit stress prediction of fiber-reinforced CMCs with stochastic loading. This book helps the material scientists and engineering designers to understand and master the damage and fracture of ceramic-matrix composites under stochastic loading.

Ceramic Matrix Composites: Lifetime and Strength Prediction Under Static and Stochastic Loading focuses on the strain response and lifetime prediction of fiber-reinforced ceramic-matrix composites under stress-rupture loading at intermediate temperatures. Typical damage mechanisms of matrix cracking, interface debonding and oxidation, and fiber's oxidation and fracture are considered in the micromechanical analysis. Effects of composite's constituent properties, peak stress, and testing temperature on the composite's strain response and lifetime are also analyzed in detail. Finally, a comparison of constant and different stochastic stress spectrum on composite's damage evolution and fracture is discussed. This book will be a practical guide for the material researcher and component designer needing to better understand the composite's damage and fracture behavior under stress-rupture loading at intermediate temperatures. - Contains detailed analysis of the stress-rupture behavior of fiber-reinforced ceramic-matrix composites - Includes experimental data on stress-rupture behavior of different CMCs - Presents micromechanical constituent models for characterizing damage and fracture behavior under stress-rupture loading - Provides data on the physical properties of each constituent at various temperatures, along with the composite's response

Nonlinear Damage Behavior of Ceramic Matrix Composites help readers [researchers, material scientists and design engineers] gain greater understanding on the damage mechanisms inside CMCs so they can better design components used in aeronautics and astronautics. Key areas addressed in the book include: the nonlinear damage behavior of ceramic-matrix composites, including damage mechanisms and models, nonlinear damage behavior of ceramic-matrix composites under tensile and fatigue loading, strain-rate dependent, stochastic loading dependent, and time dependent nonlinear damage behavior, and the effect of pre-exposure and thermal fatigue on non-linear damage behavior of ceramic-matrix composites. - Provides comprehensive coverage on damage mechanisms and models under tensile and cyclic fatigue loading which ultimately control nonlinear behavior - Covers nonlinear damage analyses of CMC components and experimental observations of damage evolution - Presents extensive knowledge on fracture mechanic principles used in the design of aerospace propulsion systems

This book focuses on mechanical hysteresis behavior in different fiber-reinforced ceramic-matrix composites (CMCs), including 1D minicomposites, 1D unidirectional, 2D cross-ply, 2D plain-woven, 2.5D woven, and 3D needle-punched composites. Ceramic-matrix composites (CMCs) are considered to be the lightweight high-temperature materials for hot-section components in aeroengines with the most potential. To improve the reliability and safety of CMC components during operation, it is necessary to conduct damage and failure mechanism analysis, and to develop models to predict this damage as well as fracture over lifetime - mechanical hysteresis is a key damage behavior in fiber-reinforced CMCs. The appearance of hysteresis is due to a composite’s internal damage mechanisms and modes, such as, matrix cracking, interface debonding, and fiber failure. Micromechanical damage models and constitutive models are developed to predict mechanical hysteresis in different CMCs. Effects of a composite’s constituent properties, stress level, and the damage states of the mechanical hysteresis behavior of CMCs are also discussed. This book also covers damage mechanisms, damage models and micromechanical constitutive models for the mechanical hysteresis of CMCs. This book will be a great resource for students, scholars, material scientists and engineering designers who would like to understand and master the mechanical hysteresis behavior of fiber-reinforced CMCs.

This book focuses on the matrix cracking behavior in ceramic–matrix composites (CMCs), including first matrix cracking behavior, matrix cracking evolution behavior, matrix crack opening and closure behavior considering temperature and oxidation. The micro-damage mechanisms are analyzed, and the micromechanical damage models are developed to characterize the cracking behavior. Experimental matrix cracking behavior of different CMCs at room and elevated temperatures is predicted. The book can help the material scientists and engineering designers to better understand the cracking behavior in CMCs.

Covering an important material class for modern applications in the aerospace, automotive, energy production and creation sectors, this handbook and reference contains comprehensive data tables and field reports on successfully developed prototypes. The editor and authors are internationally renowned experts from NASA, EADS, DLR, Porsche, MT Aerospace, as well as universities and institutions in the USA, Europe and Japan, and they provide here a comprehensive overview of current R & D with an application-oriented emphasis.

Fiber-reinforced composites have been widely applied in different industrial areas. This book focuses on the recent advances, new perspectives, and applications of different fiber-reinforced composites, such, as ceramic-matrix composites, fiber-reinforced concrete, wood–plastic composites, and so on. The design, fabrication, and application of fiber-reinforced composites are related to the high mechanical properties and nondestructive damage monitoring techniques. The experimental and damage monitoring method can reveal the internal damage evolution process inside of the fiber-reinforced composites and improve the operation reliability and safety of the composites and components. The book can help composite researchers better understand the engineering application, mechanical behavior, and damage detection of fiber-reinforced composites.